Stainless steel U tubes are manufactured by seamless or welded tube production methods, then cut to length. They are bent into U shapes using precision mandrel or rotary draw bending to ensure smooth curvature without wrinkling or thinning.
Kyaw Stainless is a reliable Naypyidaw, Myanmar-based manufacturer and supplier of high-quality stainless steel products. With a keen emphasis on precision and durability, the company provides a comprehensive array of stainless steel solutions, such as Stainless Steel U Tubes. These U Tubes, which are designed for use in heat exchangers and other high-performance applications, are renowned for their strength, corrosion resistance, and superior heat transfer characteristics. Kyaw Stainless ensures that they provide consistent products that accommodate varied industrial specifications.
Stainless Steel U Tubes are generally made up of iron, chromium (18–20%), nickel (8–12%) and trace quantities of carbon, manganese, and molybdenum, depending on the grade. These tubes possess superior corrosion resistance, particularly in high-temperature and pressure applications. They have mechanical properties of tensile strength approximately 515 MPa, yield strength 205 MPa and elongation of 35% minimum. Their high formability, toughness, and heat conductance properties recommend them for application in heat exchangers, condensers and diverse industrial applications for stable performance.
| Size Range | 10 mm OD to 50.8 mm OD |
| Stainless Steel U Tube Outside Diameter | 6.00 mm to 101.60 mm |
| Wall Thickness | 0.70 mm to 8.00 mm |
| Length | up to 20 m (65.62 ft) Length & Customed Required Length |
| Stainless Steel Heat Exchanger Tube Dimenisons | ASTM, AISI, ASME/ ANSI, JIS, DIN, EN, GB, BS, SUS |
| Standard | ASTM A 213, A 268, A 269, A 789, Equivalent to ASME, EN, JIS Etc. |
| Stainless Steel U tube Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Ti | Fe | |
| 304 | min. | 18.0 | 8.0 | |||||||||
| max. | 0.08 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | 0.10 | ||||
| 304L | min. | 18.0 | 8.0 | |||||||||
| max. | 0.030 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 12.0 | 0.10 | ||||
| 304H | min. | 0.04 | 18.0 | 8.0 | ||||||||
| max. | 0.010 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | |||||
| SS 310 | 0.015 max | 2 max | 0.015 max | 0.020 max | 0.015 max | 24.00 26.00 | 0.10 max | 19.00 21.00 | 54.7 min | |||
| SS 310S | 0.08 max | 2 max | 1.00 max | 0.045 max | 0.030 max | 24.00 26.00 | 0.75 max | 19.00 21.00 | 53.095 min | |||
| SS 310H | 0.04 0.10 | 2 max | 1.00 max | 0.045 max | 0.030 max | 24.00 26.00 | 19.00 21.00 | 53.885 min | ||||
| 316 | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| max. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| 316L | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| max. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| 316TI | 0.08 max | 10.00 14.00 | 2.0 max | 0.045 max | 0.030 max | 16.00 18.00 | 0.75 max | 2.00 3.00 | ||||
| 317 | 0.08 max | 2 max | 1 max | 0.045 max | 0.030 max | 18.00 20.00 | 3.00 4.00 | 57.845 min | ||||
| SS 317L | 0.035 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 18.00 20.00 | 3.00 4.00 | 11.00 15.00 | 57.89 min | |||
| SS 321 | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 19.00 | 9.00 12.00 | 0.10 max | 5(C+N) 0.70 max | |||
| SS 321H | 0.04 0.10 | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 19.00 | 9.00 12.00 | 0.10 max | 4(C+N) 0.70 max | |||
| 347/ 347H | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 20.00 | 9.0013.00 | |||||
| 410 | min. | 11.5 | ||||||||||
| max. | 0.15 | 1.0 | 1.00 | 0.040 | 0.030 | 13.5 | 0.75 | |||||
| 446 | min. | 23.0 | 0.10 | |||||||||
| max. | 0.2 | 1.5 | 0.75 | 0.040 | 0.030 | 30.0 | 0.50 | 0.25 | ||||
| 904L | min. | 19.0 | 4.00 | 23.00 | 0.10 | |||||||
| max. | 0.20 | 2.00 | 1.00 | 0.045 | 0.035 | 23.0 | 5.00 | 28.00 | 0.25 | |||
| Stainless Steel U tube Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 304/ 304L | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 304H | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 40 % |
| 310 / 310S / 310H | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 40 % |
| 306/ 316H | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 316L | 8.0 g/cm3 | 1399 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 317 | 7.9 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 321 | 8.0 g/cm3 | 1457 °C (2650 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 347 | 8.0 g/cm3 | 1454 °C (2650 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 904L | 7.95 g/cm3 | 1350 °C (2460 °F) | Psi 71000 , MPa 490 | Psi 32000 , MPa 220 | 35 % |
Contact us to get a quick quote for your requirement.
Our utmost concern in regards to the quality of our Stainless Steel U Tubes is client satisfaction. In order to maintain this, we apply a rigorous quality control regime to all our products. These consist of hardness testing, chemical analysis by means of spectro analysis, positive material identification (PMI), flattening tests, micro and macro tests, pitting resistance tests, flaring tests and intergranular corrosion (IGC) tests.
Stainless steel U tubes are manufactured by seamless or welded tube production methods, then cut to length. They are bent into U shapes using precision mandrel or rotary draw bending to ensure smooth curvature without wrinkling or thinning.
Stainless steel U tubes should be stored in a clean, dry area away from corrosive environments, handled with care to avoid scratches or dents, and regularly inspected and cleaned to prevent contamination or moisture buildup that can lead to corrosion.
Stainless steel U tubes are available in outer diameters ranging from 6mm to 38mm (or 1/4″ to 1 1/2″) with wall thicknesses typically between 0.5mm to 3mm, and can be customized based on application needs.
Stainless Steel U Tubes find extensive application in heat exchangers, condensers, and boilers in industries like power generation, petrochemical, oil and gas and chemical processing. Their U shape facilitates efficient heat transfer in small spaces, and hence they are suitable for high-pressure and high-temperature applications. They are also applied in marine and aerospace industries owing to their strength and corrosion resistance. Their resistance and heat handling qualities make them fundamental elements in both commercial and industrial heat exchange devices.